Fluorescent White OLEDs with a High Color-rendering Index Using a Silicon- Cored Anthracene Derivative as a Blue Host

Fluorescent white organic light-emitting diodes showing high color-rendering indices (CRIs) of up to 81 was demonstrated,with a silicon-cored anthracene derivative (PATSPA) doped with DPAVBi utilized as the deep-blue host and dye materials, and the commercial dyes rubrene and DCM2 utilized as the orange- and red-light-emitting dyes. The devices, consisting of three emissive layers, showed bright-white-light emission, but the ratio of the blue peak to the orange and red peaks changed with the current density and the thickness of the blue emissive layer. A high CRI was achieved with the use of a deep-blue emitter doped in a novel host and by optimizing the blue-layer thickness. The device with a blue-layer thickness of 10 nm showed the Commission Internationale de l'Eclairage (CIE) color coordinate of (0.33, 0.35), a high CRI of 81, and a moderate external quantum efficiency of 2% at a current density of 2.5 mA/cm2.