AISI M2 파우더를 이용한 SKD61 재질의 레이저 메탈 디포지션 기초 특성 분석

In this study, AISI M2 powder was selected primarily through various pieces of literature in order to improve the hardness and wear resistance. Among the laser metal deposition parameters, laser power was studied to improve the deposition efficiency in the laser metal deposition using a diode-pumped disk laser. An SKD61 hot work steel plate and AISI M2 powder were used as a substrate and powder for laser metal deposition, respectively. Experiments for the laser metal deposition were carried out by changing the laser power and track layer. The quality of the track surface and cross-section after applying the single-layer method was better than that obtained from applying the multi-layer method. As the laser power increased, the track thickness was increased, and the surface roughness deviation was decreased. In laser power condition of 1.6kW, the maximum hardness of the deposition track was 790Hv. This value was 40% better than the hardness of the SKD61 after heat treatment.