수용성 Cyclcophosphazene 유도체를 이용한 견섬유의 이중경화형 방염가공
Dual-curable Flame-Retardant Finish of Silk Fabrics Using a Water-soluble Cyclophosphazene Derivative
김정환(금오공과대학교); 백지윤(금오공과대학교); 장진호(금오공과대학교)
34권 4호, 217~223쪽
초록
Flame-retardant finished silk fabrics could release carcinogenic formaldehyde resulting from the conventional finishing agents. New water-soluble cyclophosphazene derivative can be used as a formaldehyde-free flame retardant for the silk protein. Dichloro tetrakis{N-[3-dimethylamino)propyl]methacrylamido}cyclophosphazene(DCTDCP) can be cured by heat or UV irradiation as a durable flame retardant for the silk fabrics. Treatment conditions were optimized including curing temperature and time, finishing formulations, and UV energy. At the 30% DCTDCP application, peak HRR and THR decreased by 42.6% and 49.6% respectively compared to the pristine silk fabrics. Also char residue increased up to 48% from 11% indicating solid-phase retarding mechanism. The flame-retardant silk fabrics showed a LOI of 31.1 and the washed sample maintained a LOI of 26.8 even after ten laundering cycles.
Abstract
Flame-retardant finished silk fabrics could release carcinogenic formaldehyde resulting from the conventional finishing agents. New water-soluble cyclophosphazene derivative can be used as a formaldehyde-free flame retardant for the silk protein. Dichloro tetrakis{N-[3-dimethylamino)propyl]methacrylamido}cyclophosphazene(DCTDCP) can be cured by heat or UV irradiation as a durable flame retardant for the silk fabrics. Treatment conditions were optimized including curing temperature and time, finishing formulations, and UV energy. At the 30% DCTDCP application, peak HRR and THR decreased by 42.6% and 49.6% respectively compared to the pristine silk fabrics. Also char residue increased up to 48% from 11% indicating solid-phase retarding mechanism. The flame-retardant silk fabrics showed a LOI of 31.1 and the washed sample maintained a LOI of 26.8 even after ten laundering cycles.
- 발행기관:
- 한국염색가공학회
- 분류:
- 염색공학